rPLA Filament – S2
Price range: 46.75 PLN through 60.00 PLN gross
Fiberlogy R PLA is an eco-friendly 3D printing filament made from 100% recycled material sourced from carefully selected suppliers. It combines high print quality with minimal environmental impact. The product may vary in shade and contain trace amounts of glitter, which is due to the nature of the raw material. Ideal for environmentally conscious users seeking sustainable solutions.
Fiberlogy R PLA is the answer to the growing ecological and environmental needs of 3D printing users. This innovative filament is made from 100% recycled material sourced exclusively from verified and carefully selected sources. As a result, Fiberlogy R PLA combines high print quality—on par with standard PLA filaments—with a commitment to environmental sustainability.
Filament production is strictly controlled at every stage—from material sourcing, through storage, to the final product that reaches customers’ 3D printers. This approach guarantees consistent properties and safe, reliable printing.
It is worth noting that due to natural variations in the raw material, Fiberlogy R PLA filament may vary in color and contain trace amounts of glitter, which attests to its authentic, recycled origin. The availability of the material depends on the availability of recycled raw materials, which ensures that production is in line with the principles of sustainable development.
Fiberlogy R PLA is an excellent choice for 3D printing users who want to combine quality with care for the planet and support eco-friendly innovations in additive manufacturing.
Printing Parameters
- Printing temperature: 210–230°C
- Bed temperature: 60°C
- Bed material: Smooth PEI, Textured PEI, Glass
- Curing conditions: 50°C / 4 hours
- Enclosed chamber: not required
- Humidity: 75–100%
Technical Specifications
- Density: 1.24 g/cm³
- Heat deflection temperature under load @ 0.45 MPa: 55°C (ASTM E2092)
- Glass transition temperature: 55–60°C (DSC)
- Tensile strength at yield: 60 MPa (ASTM D882)
- Tensile strength at break: 53 MPa (ASTM D882)
- Tensile modulus: 3,500 MPa (ASTM D882)
- Izod impact strength (notched) @ 23°C: 16 J/m (ASTM D256)
- Flexural strength: 81 MPa (ASTM D790)
- Flexural modulus: 3,800 MPa (ASTM D790)
- Elongation at yield: 6% (ASTM D882)
-