FiberSmooth PVB Filament - S2
Wiping or soaking the model in IPA results in a smooth, glossy surface.
Low shrinkage reduces the risk of deformation and delamination from the table.
Low shrinkage ensures precise dimensions and better detail reproduction.
Fiberlogy FiberSmooth is an innovative 3D printing filament from the PVB family that produces smooth, glossy prints with a porcelain-like finish. Its greatest advantage is how easily it can be smoothed with isopropyl alcohol (IPA). When immersed in the liquid or exposed to its vapors, the model partially dissolves, causing the outer contours to bond more effectively and successfully mask layer lines.
FiberSmooth produces prints with an elegant, glossy surface that gives projects a professional look. The material masks the imperfections of additive manufacturing, ensuring that every model looks aesthetically pleasing and uniform.
FiberSmooth filament prints similarly to PLA, making it beginner-friendly. Thanks to its low shrinkage and odorless nature, printing is comfortable, though a higher bed temperature is recommended to improve interlayer adhesion and prevent the model from peeling off.
FiberSmooth is ideal for decorative projects, model making, prototyping, and any application where an aesthetically pleasing, smooth finish is essential. It is perfect for ornaments, figurines, architectural models, and design elements.
Fiberlogy FiberSmooth is the ideal filament for 3D printer users who want to combine the ease of printing with PLA with the ability to achieve a porcelain-smooth and glossy surface—a great choice for decorative and artistic projects.
-
The ability to smooth using isopropyl alcohol (IPA)
Wiping or soaking the model in IPA results in a smooth, glossy surface.
-
Low contraction
Low shrinkage reduces the risk of deformation and delamination from the table.
-
Ease of printing
Low shrinkage ensures precise dimensions and better detail reproduction.
Printing Parameters
- Printing temperature: 215–225°C
- Bed temperature: 75°C
- Bed material: Smooth PEI + adhesive; Textured PEI; Glass + adhesive
- Curing conditions: 40°C / 4 hours
- Enclosed chamber: not required
- Humidity: 75–100%
Technical Specifications
- Density: 1.1 g/cm³
- Vicat softening temperature: 70°C (ISO 306)
- Heat deflection temperature @ 1.8 MPa: 55°C (ISO 75)
- Glass transition temperature: 70°C (DSC)
- Tensile strength at break: 51 MPa (ISO 527)
- Tensile modulus: 3050 MPa (ISO 527)
- Flexural strength: 77 MPa (ISO 178)
- Flexural modulus: 2,350 MPa (ISO 178)
- Elongation at break: 88% (ASTM D638)
- Charpy impact strength (unnotched) @ 23°C: 110 kJ/m² (ISO 179)