ABS Plus Filament - S2
Its increased hardness and tensile strength allow it to withstand greater loads without deformation or microcracks.
The material absorbs impact energy without cracking or shattering.
It maintains dimensional stability at elevated temperatures and does not undergo thermal deformation.
The print can be machined, as well as glued, painted, or smoothed with solvent vapor.
Lower shrinkage allows for printing without the need for an enclosed printer.
Filament available in the new spool system. Compatible with BambuLab AMS.
ABS PLUS is a modern engineering filament for 3D printing that combines high strength with ease of use. Compared to standard ABS, it features increased mechanical strength and less shrinkage during printing, which results in more stable and precise prints.
One of the key advantages of ABS PLUS is an easier and faster printing process—the material does not require a closed chamber, yet still produces parts with high durability and excellent detail reproduction. Additionally, this filament is suitable for machining, which expands its range of applications.
ABS PLUS is widely used in industry—from creating advanced prototypes, through the production of high-strength parts, to final end-use products requiring high durability and load-bearing capacity.
-
Increased hardness and strength
Its increased hardness and tensile strength allow it to withstand greater loads without deformation or microcracks.
-
High impact strength
The material absorbs impact energy without cracking or shattering.
-
Resistance to high temperatures and scratches
It maintains dimensional stability at elevated temperatures and does not undergo thermal deformation.
-
Capability for mechanical and chemical processing
The print can be machined, as well as glued, painted, or smoothed with solvent vapor.
-
Compatibility with open printers
Lower shrinkage allows for printing without the need for an enclosed printer.
Printing Parameters
- Printing temperature: 250–270°C
- Bed temperature: 100°C
- Bed material: Smooth PEI + adhesive; Textured PEI; Glass + adhesive
- Curing conditions: 60°C / 4 hours
- Enclosed chamber: recommended
- Airflow: 0–10%
Technical Specifications
- Density: 1.05 g/cm³
- Charpy impact strength (notched) @ 23°C: 18 kJ/m² (ISO 179)
- Vicat softening temperature: 97°C (ISO 306)
- Deflection temperature under load @ 1.8 MPa: 100°C (annealed) (ISO 75)
- Tensile strength at yield: 45 MPa (ISO 527)
- Tensile modulus of elasticity: 2300 MPa (ISO 527)
- Flexural strength: 68 MPa (ISO 178)
- Flexural modulus: 2,300 MPa (ISO 178)
- Elongation at break: 2.5% (ISO 527)
-
Yellow -
Black