PETG FR V0 – S2 Filament
127.90 PLN gross
Fiberlogy PET-G V0 is a flame-retardant 3D printing filament belonging to the FR (Flame Retardant) family. It combines the ease of printing typical of PET-G with fire resistance compliant with the UL94 V0* standard. Ideal for producing electronics enclosures, mechanical components, and other parts exposed to high temperatures or contact with fire.
Fiberlogy PET-G V0 is a specialized 3D printing filament from the FR (Flame Retardant) material group, designed for safe, functional prints. The material is flame-retardant in accordance with the UL94 V0* standard — it self-extinguishes in less than 10 seconds upon contact with fire, making it ideal for the production of electronics enclosures, vehicle components, and machine parts that must meet elevated fire safety standards.
Despite its fire-resistant properties, PET-G V0 retains all the advantages of traditional PET-G. The filament is easy to use and does not require an enclosed printer or a special nozzle. As a result, it can be used in both professional industrial settings and home 3D printers.
- fire resistance (UL94 V0*),
- high mechanical and thermal strength typical of PET-G,
- low shrinkage and dimensional stability of prints,
- capability to print without an enclosed chamber and at high build plate temperatures,
- hygroscopic material—be sure to dry it thoroughly before printing to avoid print quality issues.
Fiberlogy PET-G V0 is an excellent choice for projects requiring safety and functionality. It is ideal for:
- enclosures and covers for electronic devices,
- mechanical components for vehicles and machinery,
- prototypes and components requiring resistance to high temperatures and fire,
- industrial and professional projects where fire safety is critical.
*This filament is not certified by Underwriters Laboratories and does not have a UL number.
Non-flammable – safe when exposed to open flames
Halogen-free – does not emit harmful fumes or odors
High chemical resistance
Low susceptibility to spasm
Ease of printing
Printing Parameters
- Printing temperature: 220–250°C
- Bed temperature: 90°C
- Bed material: Smooth PEI + adhesive; Textured PEI; Glass + adhesive
- Curing conditions: 60°C / 4 hours
- Enclosed chamber: not required
- Airflow: 0–25%
Technical Specifications
- Density: 1.26 g/cm³
- Charpy impact strength (notched) @ 23°C: 3 kJ/m² (ISO 179)
- Vicat softening temperature: 70°C (ISO 306)
- Heat deflection temperature under load @ 1.8 MPa: 58°C (ISO 75)
- Heat deflection temperature under load @ 0.45 MPa: 63°C (ISO 75)
- Tensile strength at yield: 40 MPa (ISO 527)
- Tensile strength at break: 25 MPa (ISO 527)
- Tensile modulus of elasticity: 2,350 MPa (ISO 527)
- Elongation at yield: 3.3% (ISO 527)
- Elongation at break: 40% (ISO 527)