Fiberlogy Nylon PA12+CF is a technical filament reinforced with 15% carbon fiber. It combines low weight with exceptional stiffness, high heat resistance, and lower shrinkage than standard PA12 nylon. Ideal for industrial and engineering applications.
Fiberlogy Nylon PA12+CF is an advanced technical filament designed for the most demanding engineering and industrial projects. It is based on Nylon PA12, reinforced with 15% carbon fiber, which gives it unique mechanical and functional properties.
Thanks to its carbon fiber content, the filament offers significantly greater stiffness and mechanical strength while reducing the weight of the components. This makes the printed parts both lightweight and highly durable.
Compared to standard PA12 nylon, the carbon fiber version offers better resistance to high temperatures and less shrinkage during printing. As a result, it is easier to achieve precise, dimensionally stable prints, even with complex geometries.
Fiberlogy PA12+CF is a filament designed for professionals. It is ideal for:
- the automotive industry—for lightweight yet durable structural components,
- engineering and mechanics—for functional prototypes and technical parts,
- aviation and drones—where low weight and high durability are crucial,
- the production of final components that must combine aesthetics, strength, and resistance to external conditions.
For printing with Nylon PA12+CF filament, we recommend using a 3D printer with an enclosed and heated chamber to ensure process stability and high-quality finished models.
-
High mechanical strength and stiffness
The print retains its shape even under significant mechanical stress.
-
Low contraction
Low shrinkage reduces the risk of deformation and delamination from the table.
-
Temperature resistance up to 160°C
The print retains its shape at temperatures up to 160°C without warping.
-
Lower susceptibility to moisture
PA12 is less prone to absorbing moisture than, for example, PA6 filaments
Printing Parameters
- Printing temperature: 255–270°C
- Bed temperature: 110°C
- Bed material: Smooth PEI + adhesive; Textured PEI + adhesive; Glass + adhesive
- Curing conditions: 80°C / 4 hours
- Enclosed chamber: not required
- Airflow: 0–10%
Technical Specifications
- Density: 1.07 g/cm³
- Charpy impact strength (notched) @ 23°C: 15 kJ/m² (ISO 179)
- Heat deflection temperature under load @ 1.8 MPa: 150°C (ISO 75)
- Heat deflection temperature under load @ 0.45 MPa: 170°C (ISO 75)
- Tensile strength at break: 120 MPa (ISO 527)
- Tensile modulus: 7,300 MPa (ISO 527)
- Elongation at break: 5% (ISO 527)
- Charpy impact strength (unnotched) @ 23°C: 75 kJ/m² (ISO 179)
-